Nano-fibers of the $Li[Ni_{1/3}Co_{1/3}Mn_{1/3}]O_2$ electrode were synthesized from a metal oxide precursor using the electrospun method. The XRD patterns of all prepared powders showed a hexagonal ${alpha}$ - $NaFeO_2$ structure (space group: R-3 m, 166). Scanning electron microscopy showed that all the synthesized samples were comprised of nanofibers with a size of 100~800 nm. Among the samples tested, the calcined $Li[Ni_{1/3}Co_{1/3}Mn_{1/3}]O_2$ nanowires in oxygen heating atmosphere showed a high charge and discharge capacity of 239.22 and 172.81 $mAhg^{-1}$ at the $1^{st}$ cycle, respectively. In addition, the charge transfer resistance was also improved significantly compared to the other samples.