$(1-x)BaTiO_3+(x)Cd_5(PO_4)_3Cl$ ceramics were prepared by the conventional ceramic technique, i.e., solid state reaction at high temperature. The concentration of $Cd_5(PO_4)_3C$ was varied from 0.01 to 0.15 mole fraction. In order to study the phase transitions of our ceramics, the Raman scattering spectra were measured as functions of concentration x and temperature. It was found that the soluble limit of $Cd_5(PO_4)_3Cl$ in $BaTiO_3$ was the x=0.05 composition and $BaTiO_3$ phase disappeared above x=0.10. A new phase identified as $Ba_4Ti_3P_2O_{15}$ was detected in all samples of our compositions. The Curie temperature shifts up to $130^{circ}C$ as the concentration x increases from zero to 0.05 and shift down to $95^{circ}C$ as further increases to 0.08. For the increase of the Curie temperature, it is suggested that it can result from the inhibition of displacement of $Ti^{4+}$ in the distorted octahedron due to well dispersed $Ba_4Ti_3P_2O_{15}$ and $Cd_5(PO_4)_3Cl$ phase.