Polymer electrolyte membrane fuel cell (PEMFC) performance degrades when hydrogen sulfide ($H_2S$) is present in the fuel hydrogen gas; this is referred to as $H_2S$ poisoning. This paper reveals $H_2S$ poisoning on PEMFC by measuring electrical performance of single cell FC under various operating conditions. The severity of $H_2S$ poisoning depended on $H_2S$ concentration under best operating conditions($65^{circ}C$ of cell temperature and 100% of anode humidification). $H_2S$ adsorption occured on the surface of catalyst layer on MEA, but not on the gas diffusion layer(GDL) by analyzing SEM/EDX data. In addition, MEA poisoning by $H_2S$ was cumulative but reversible. After poisoning for less than 150 min, performance of PEMFC was recovered up to 80% by just inert nitrogen gas purging.