Lead-free (1-x)$(Na_{0.5}K_{0.5})NbO_3-xLiNbO_3$, i.e., NKN-LNx (x=0.0, 0.1, 0.2, 0.3, 0.4 mol) was prepared using the conventional solid state reaction method. The effects of LN mixing on the ferroelectric properties of NKN-LNx ceramics were studied using a dielectric constant and P-E (Polarization-electric field) measurements. Ferroelectricity was observed in the composition for x approximately varying between 0.0 and 0.4. Minimum remanent polarization $2P_r=5C/cm^2$ was achieved in the composition for x = 0.2. The ferroelectric phase transition temperature $T_C$ increased with increasing LN content. The ferroelectric phase transition of NKN-LNx ($x{geq}0.1$) is a second-order phase transition, and that of NKN-LNx ($x{leq}0.2$) is a first-order phase transition. These results indicate that the ferroelectric phase transition temperature of NKN-LNx change from that of second-order to weak first-order phase transition according to the LN content.