In this study, Cu-2.5at.%Ni-1at.%Si alloys were fabricated by horizontal continuous casting system to improve the electrical conductivity and mechanical properties of Cu-Ni-Si alloy. Withdrawing speed was changed with 50, 100, 150 and 200 mm/min for the optimum manufacturing condition. Microstructure was observed using OM, FE-SEM and TEM. Electrical conductivity was measured by 4-point probe method and mechanical properties were tested. A horizontal continuous cast thin slab had sound macro and micro structures with partly crystallized structures. Electrical resistivity decreased with increasing annealing temperature from 250 to $850^{circ}C$, with increasing annealing temperature The maximum hardness and tensile strength were Hv 130, 610 MPa at $550^{circ}C$, respectively. With changing withdrawing speed from 50 to 150 mm/min, hardness, tensile strength, yield strength and elongation were Hv 60-65, 210-230 MPa, 65-75 MPa and 40-50%, respectively.