In this study domestic thinning and small diameter woods of Giant dogwood (Cornus controversa Hemsl) was used. To increase the utilizability of wood, the utilizability was proposed after manufacturing laminated wood by pressing and heating. The physical and mechanical characteristics of Laminated wood were investigated and the color change was measured, using a Chromaticity coordinates, after being pressed at 10% (45 mm), 20% (40 mm), 30% (35 mm) for 5 minutes, using Stopper, and then heated at $180^{circ}C$ for 6, 12, 24 and 48 hours. The results were as follows. Wood density, compressive strength, MOR, MOE are increased with increasing pressing rate but decreased as heating time is increased after pressing. However, Color change is clear, dimensional stability is improved after pressing and heating.