$MgB_2$ superconducting sheets have been fabricated by powder rolling method using mixture of Mg and B powders. Sheet-type $MgB_2$ bulk samples of ~10 mm width and 50-100 mm long were squeezed out after compacted by two rotating rolls of 130 mm diameter with gap distance of 0.5 mm and speed of ~40 cm/min (~1 rpm). The nominal composition of Mg, which is ductile metal, was added up to 30% to facilitate forming the $MgB_2$ sheets. The annealed samples at $900^{circ}C$ and 3 hrs showed superconducting transition temperature of ~32 K and critical current densities at zero fields were ${sim}10^5A/cm^2$ at 5 K and ${sim}5{ imes}10^4A/cm^2$ at 20 K.