We prepared the highly ordered nano-wires of polypyrrole, polyaniline conductive polymers and polypyrrole/ polyaniline conductive copolymers by templating the anodic aluminum oxide (AAO) porous membrane, in which pore diameter was 20 nm, 100 nm and 200 nm. Those conductive polymers were grown from pore inner surface of AAO membrane forming hollow tubes and then wire structures were formed after 3 hour polymerization. By removing AAO membrane templates using sodium hydroxide solution, the conductive polymer nano-wires were successfully obtained, of which diameter and length were close to the ones of nano-pores in AAO membrane template. Crystallinity and thermal stability of the conductive polymer nano-wires were higher than irregular ones that prepared by solution polymerization. Furthermore, the electrical resistance of conductive polymer nano-wires were reduced by about 4~60% compared with that of the irregular polymers prepared by solution polymerization.