Melt copolymerization reactions of several bis(diethylamino)silane derivatives, bis(diethylamino)methylphenylsilane, bis(diethylamino)methyloctylsilane, 1,2-bis(diethylamino)tetramethyldisilane, and 1,3-bis(diethylamino) tetramethyldisiloxane, with 2,7-dihydroxyfluoren-9-one were carried out to yield poly[oxy(2,7-fluoren- 9-onenylene)oxy(diorganosilylene)]s bearing the fluoren-9-one fluorescent aromatic group in the polymer main chain: poly[oxy(2,7-fluoren-9-onenylene)oxy(methylphenylsilylene)], poly[oxy(2,7-fluoren-9-onenylene) oxy(methyloctylsilylene)], poly[oxy(2,7-fluoren-9-onenylene)oxy(tetramethyldisilylene)], and poly[oxy- (2,7-fluoren-9-onenylene)oxy(tetramethyldisiloxanylene)]. These polymeric materials are soluble in common organic solvents such as $CHCl_3$ and THF. FTIR spectra of all the materials reveal characteristic Si-O-C stretching frequencies at 1012-1018 $cm^{-1}$. In the THF solution, the prepared materials show strong maximum absorption peaks at 258-270 nm, strong maximum excitation peaks at 260-280 nm, and strong maximum fluorescence emission bands at 310-420 nm. TGA thermograms suggest that most of the polymers are essentially stable to $200^{circ}C$ without any weight loss and up to $300^{circ}C$ with only a weight loss of less than 5% in nitrogen.