The computer simulation was performed to confirm distribution of current and power density according to inner diameter of graphite mold of SPS(Spark Plasma Sintering). When the inner diameters of a graphite mold are varied $10mm{Phi}$, $20mm{Phi}$, $30mm{Phi}$ and $40mm{Phi}$, the more the inner diameter of graphite mold is decreased, the more the current density of punch section is increased. Because the electrical resistivity of the SiC-$ZrB_2$ specimen section($7.77{ imes}10^{-4}{Omega}{cdot}cm$) was lower than the electrical resistivity($6.00{ imes}10^{-3}{Omega}{cdot}cm$) of graphite section, the current density and power density of specimen section was higher than those of graphite section. It is considered that a SiC-$ZrB_2$ composite is sintered by more Joule heat of specimen section than that of mold and punch section. The current and power density distribution of a SiC-$ZrB_2$ composite can be predicted through computer simulation when SPS is conducted, and an electrical resistivity of the SiC-$ZrB_2$ composite is main element of SPS.