Effect of Cu and $DyF_3$ powder mixing with Cu-free (Nd, Dy)-Fe-B jet-milled powder on the magnetic properties of sintered magnets was investigated. The coercivity of a magnet prepared from the Cu-free (Nd, Dy)-Fe-B powder was about 10 kOe even though the alloy powder already contained some Dy (3.5 wt%). When small copper powder was blended, however, the coercivity of the magnet increased almost 100%, exhibiting about 20 kOe. On the contrary, the coercivity enhancement was moderate, about 4 kOe, when dysprosium content in the sintered magnet was simply increased to 4.9 wt% by the addition of small $DyF_3$3 powder.