The aim of this study was to investigate the effects of forming depth on the deformation behavior of cup-like tubes made of AISI1020 steel in tube spinning process. Spinning process was performed on cup-like tubes, which had an inner diameter of 34mm and thicknesses of 7, 8.5 or 11.5mm. The forming depths achieved were 3, 4, and 5.5mm. The complex deformation behaviors occurring during the tube spinning process was explained using the experimental results. Also analyzed were the causes of the material buildup and the bulge defect of inner surface, observed on cross section of tubes. The relationship between tube spinning conditions and the height of bulge defect was examined. The results indicate that bulge defect is increased with a decrease of the forming depth. Moreover, a critical forming depth exists for preventing the generation of the bulge defect in the tube spinning process. The present results will be useful for future decisions of forming depths for successful tube spinning of cup-like tubes.