The Microstructure and nonlinear electrical properties of the ZPCCYT (ZnO-$Pr_6O_{11}$-CoO-$Cr_2O_3$-$Y_2O_3$-$Tb_4O_7$) varistors were investigated for different amounts of $Tb_4O_7$. The addition of $Tb_4O_7$ has a significant effect on microstructure and electrical properties. Analysis of the microstructure indicated that the ceramics consisted of ZnO grain as a main phase and a few secondary phases as a mix of $Pr_6O_{11}$, $Y_2O_3$, and $Tb_4O_7$. As the amount of $Tb_4O_7$ increased, the sintered densities of pellets increased from $ ho$ = 5.70 to $5.78g/cm^3$ and the average grain size decreased from d = 4.8 to $3.6{mu}m$. The increase in the amount of $Tb_4O_7$ increased from $E_B$ = 7,473 to 10,035 V/cm and from ${alpha}$ = 39.7 to 52.2. In particular, it was found that the ceramics modified with 1.0 mol% in the amount of $Tb_4O_7$ are suited for the varistors for high voltage in the light of a high sintered density and a high voltage gradient.