Steel corrosion is one of the most critical deteriorations in concrete structures due to the problems associated with both durability and structural safety issues. For protection of steel against corrosion problems, researches to improve concrete durability and steel corrosion protection such as rebar coating by hot-dip galvanizing steel have been carried out. This study was performed to quantitatively evaluate anti-corrosion and structural performance of concrete structures reinforced with hot-dip galvanizing steel rebar. Preliminary tests for several metal coatings such as zinc, aluminum, and their alloy (Zn 45% + AL 55%) were performed. After evaluation of corrosive characteristics, Zn was selected for the coating material and the corrosion behaviors in Zn-coated steel were evaluated in various conditions. Furthermore, tensile and adhesive strengths were evaluated for the normal and the hot-dip galvanized steel. The crack patterns and structural behaviors of RC specimens with the normal and coated steel were investigated. Also, corrosion characteristics including corrosion in various coating metal and potential change in metal with notch were evaluated. Structural performances of tensile and adhesive strengths as well as RC beam behavior under flexural/shear loading were evaluated. The test and evaluation results showed that the applicability of hot-dip galvanized steel rebar can be used as corrosion resistant reinforcements for RC structures.