This research is based on fabricating Cu(In,Ga)$Se_2$ thin-film by co-evaporation method. On $1^{st}$ - stage, $In_2Se_3$ phase appeared when the substrate temperature reached to $400^{circ}C$, however, there was small effect between the substrate temperature and absorbency spectrum on $2^{nd}$, $3^{rd}$ - stage because the average thickness of the thin-film was $1{mu}m$ or higher. SEM and XRD was measured on $2^{nd}$ and $3^{rd}$ stage and it showed as the substrate temperature increases, the density of the crystal structure increased with the decreament of the vacancy. Furthermore, the formation of Cu(In0.7Ga0.3)$Se_2$ phase showed at $480^{circ}C$ and $500^{circ}C$.