The corrosion properties of anodized films on aluminium 6070 alloy in a sulfuric acid have been studied. Comparison to evaluate the anodized A6070 and pure 6070 specimen, corrosion tests in $HNO_3$ vapor environment of the 20 wt.% were performed up to 72 hours. Characteristics of film formation and surface morphology were examined by optical microscopy, FE-SEM, and EDS. The oxide film anodized in the sulfuric acid solution contained 5 to 10 wt.% of sulfur. In the initial stages of corrosion, anodized specimens exhibited corrosion resistance than the pure specimen. However, the corrosion conditions in 24 hours, corrosion was far more anodized specimen than pure specimen. Therefore, anodized films contained sulfur, nitric acid vapor in the environment is thought to stimulate corrosion.