Duplex stainless steels have the dual microstructure of austenite and ferrite phases. This steel exhibits generally a high corrosion resistance and higher mechanical strength compared with austenitic stainless steels. The steels used in the investigation have the chemical composition of Fe-22Cr-xNi-yMn-0.2N in which the contents of Ni and Mn were varied with maintaining the equal [Ni/Cr] equivalent. The fraction of ferrite phase was increased with the increase of annealing temperature. The impact factor of Mn element on the [Ni] equivalent was amended on the basis of the results of the investigation. 4Mn-2Ni alloy showed the highest pitting corrosion resistance. The fraction ratio, grain size and misorientation angle between grains were measured, and the correlation with pitting potential was investigated.