The magnetic interaction effect on the magnetic activation volume and area of electrodeposited CoPt magnetic films was investigated. The dipolar interaction was predominant interaction mechanism for all samples. And the interaction strength was increased with decreasing current density and increased with increasing sample thickness. Although the activation volumes of the samples fabricated at low current density were larger than those of the high current density samples, the sample thickness seemed to have little influence on the variation of activation volume. But it was found that the activation area was apparently affected by the magnetic interaction strength as well as the current density.