Purpose: This study is to provide basic data of the dental acrylic denture base resin in the mechanical property difference investigation according to the monomer composition weight ratio of the acrylic denture base resin. Methods: The monomer composition of the acrylic denture base resin and weight ratio makes the different specimen. It measured the mechanical property with the specimens through Hardness Test, Tensile Test, Flexural Test, Flexural Modulus, FT-IR Test. Results: The control group Vertex was 18.4 Hv and the experimental group MED was 14.46~19.07Hv in the hardness test. Vertex was 364N, MED-3 was lowest in the tensile strength test and the Head of a family cursor declination was big. The result declination of the experimental specimens showed. Vertex and MED-2 was the highestest in the flexural test and after coming MED-6, MED-5, MED-1, MED-3, MED-4. Vertex and MED-2, as to a spectrum for $500{sim}1800cm^{-1}$ peak can show the excellent degree of polymerization in the FT-IR Test. Conclusion: The ideal weight ratio of the monomer of the acrylic denture base resin of which the mechanical property is the highestest was MMA 100g, EDGMA 5g, DMA 0.2g, of MED-2.