Partially hydrolyzed cellulose acetate (CA) fibers were prepared by treating CA fibers in aqueous $Na_2CO_3$ solutions of various concentrations. The deacetylation of CA fibers was confirmed through FTIR spectra and WAXD patterns. The hydrolysis was confined to the surface part of the CA fiber by controlling the treatment conditions. The resultant fibers had a sheath-core structure with a sheath component of regenerated cellulose and a core of non-hydrolyzed cellulose acetate. The SEM images of the surface-hydrolyzed CA fibers, the core of which was dissolved out using acetone as the solvent, showed that the sheath thickness increased with increasing alkaline concentration, indicating an increase in the hydrolyzed fiber, i.e., regenerated cellulose. Polarized FTIR analysis of the polyimide film rubbed with velvet fabrics of surface-hydrolyzed CA fibers showed that polyimide molecules were preferentially oriented to the rubbing direction.