In this study, green barium strontium silicate phosphor ($BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$) was synthesized using a solid-state reaction method in air and reducing atmosphere. Investigation of the firing temperature indicates that a single phase of $BaSrSiO_4$ is formed when the firing temperature is higher than $1400^{circ}C$. The effect of firing temperature and doping concentration on luminescent properties are investigated. The light-emitting property was the best when the molar content of $Eu_2O_3$ was 0.025 mol. Also, the luminescent brightness of the $BaSrSiO_4$ fluorescent substance was the best when the particle size of the barium was $0.5{mu}m$. $BaSrSiO_4$ phosphors exhibit the typical green luminescent properties of $Eu^{3+}$ and $Eu^{2+}$. The characteristics of the synthesized $BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$ phosphor were investigated using X-ray diffraction (XRD) and scanning electron microscopy. The maximum emission band of the $BaSrSiO_4:Eu^{3+}$, $Eu^{2+}$ was 520 nm.