Rare earth ions, either $Eu^{3+}$ or $Dy^{3+}$-doped $CaMoO_4$ phosphors were synthesized by using the solid-state reaction method. The crystalline structure of all the phosphor powders, irrespective of the type and concentration of activator ions, was found to be a tetragonal system with the main diffraction peak at (112) plane. For $Eu^{3+}$-doped $CaMoO_4$ phosphors, the grain particles showed an increasing tendency and the pebble-like patterns with a very homogeneous size distribution in the range of 0.01~0.10 mol of $Eu^{3+}$ ions concentration, and the excitation spectra were composed of a broad band centered at 311 nm and weak multiline peaked in the range of 360~470 nm. The dominant emission spectrum was the strong red emission centered at 618 nm due to the $^5D_0{ ightarrow}^7F_2$ transition of $Eu^{3+}$ ions. For $Dy^{3+}$-doped $CaMoO_4$ powders, excitation spectra showed a charge transfer band centered at 303 nm and relatively weak bands resulting from the transitions of $Dy^{3+}$ ions and the main yellow emission spectrum was observed at 578 nm, which was assigned to the $^4F_{9/2}{ ightarrow}^7H_{13/2}$ transition of $Dy^{3+}$ ions.