First, a purified sludge was calcined at various temperatures viz. 800, 900, 1000, 1100 and $1200^{circ}C$ per hour. Subsequently 100 wt% of ware from Geryong mountain was mixed with 5~25 wt% of a purified sludge. Then the ware was treated at $1250^{circ}C$ in an electric kiln to test a bending strength. The physicochemical property of the prepared ware was characterized by XRD, Raman and SEM analysis. Among the different percentage, 25 wt% of a ware in a purified sludge calcined at $1000^{circ}C$ showed 689 $kg/cm^2$ strength. Also the purified sludge calcined at $1000^{circ}C$ was adequate physical properties than the other composites. Further to enhance the physical strength, 3 wt% $TiO_2$ (a mineralizer) was added into the ware and the strength was increased up to 731 $kg/cm^2$. The composites exhibit absorption and porosity rates of 0.17% and 0.39% respectively.