The purpose of this study is to fabricate the flame retardant polyester fabric by thermal bonding with low melting component of flame retardant bicomponent filament(LMFRPC) and to describe the characteristics of thermal bonded fabrics. The fabrics were prepared with flame retardant polyester filaments(FRP) as warp and blended filaments of FRP and LMFRPC as weft. The LMFRPC have a sheath and a core wherein the core comprises a flame retardant polyester and the sheath comprises a thermoplastic polyester of low-melting point. In this study, we investigated the physical properties, melting behavior of filament, the effect of the component of FRP and LMFRPC on the thermal bonding, mechanical properties. Melting peak of LMFRPC showed the double melting peak. The thermal bonding of the fabric formed at lower melting peak temperature of bicomponent filament of LMFRPC. The optimum thermal bonding conditions for fabrics was applied at about $170^{circ}C$ for 60 seconds by pin tenter. On the other hand, the tensile strength, elongation, and LOI of the fabric increased with an increasing component of FRP of weft.