A polymeric photobase generator containing oxime-urethane groups is applied to a fluorescence micropatterning material. Polymer bearing oxime-urethane groups was prepared by copolymerization of methyl methacrylate with methacryloyloxyethyl benzophenoneoxime urethane (MBU). The reaction of amino groups in the irradiated copolymer film with dansyl chloride (Dns-Cl) was monitored by using UV absorption, IR absorption and fluorescence spectroscopy. The fluorescence spectrum of the Dns-Cl-treated irradiated copolymer film shows a strong fluorescence with a fluorescence maximum wavelength at 510 nm. A blue fluorescent micropattern with a line width of $2{sim}3{mu}m$ was obtained. Treatment of the irradiated copolymer film with Dns-Cl and rhodamine B mixture led to the formation of green, red, and orange-colored fluorescence micropatterns. Thus, various colored micropatterns on a single polymer film can be obtained by selective excitation of each dye molecules.