ZnO films were deposited on glass substrates by radio frequency (RF) magnetron sputtering and exposed to intense electron beam irradiation to investigate the effects of electron irradiation on the properties of the films. Although all of the films had ZnO (002) textured structure regardless of electron irradiation, the grain sizes of the films decreased with electron irradiation. Surface roughness also depended on electron irradiation. The surface roughness varied between 2.3 and 1.6 nm, depending on the irradiation energy. Based on photoluminescence (PL) characterization, the most intense UV emission was observed from ZnO films irradiated at 900 eV. Since the intensity of UV emission is dependent upon the stoichiometric of ZnO films, we conclude that 900 eV was the optimum electron irradiation energy to achieve the best stoichiometric of ZnO films in this study.