During start up and shut down of a proton exchange membrane fuel cells (PEMFC), the performance and lifetime of PEMFC were reduced. In this study, effect of startup and shutdown were investigated in dead-end type PEMFC using oxygen as a cathode gas with polarization curve, impedance spectroscopy (EIS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Dummy load which eliminates residual hydrogen and oxygen during startup and shutdown operation should be applied to mitigated the degradation of PEMFC performance. At 50% relative humidity (RH) under the repetitive on/off cycling, the cell performance decayed faster than at 100% RH because of corrosion of the cathode carbon support. Water suppling into cell reduced the degradation rate of dead-end type PEMFC during start up and shut down cycling at 50% RH.