It is characterized and classified as the type of red brown glass beads to compare the chemical composition and manufacturing technique on the 141 samples in 12 sites of the Three Kingdom Period analyzed until now. It can be divided into three types according to the chemical composition of stabilizers(CaO & $Al_2O_3$) and soda raw materials(MgO & $K_2O$) on the red brown glass beads except one sample. Type I of high alumina glass is identified as the most common types that is 78.6 % of the distribution ratio at analytical samples and is excavated the most from ruin sites. In contrast, type II, 13.6 % of distribution ratio at analytical samples, is about 5 % CaO and $Al_2O_3$, MgO and $K_2O$ at around 1.5 % is similar to the composition of plant ash glass. Type III is that the content of CaO is higher than $Al_2O_3$ and the content of MgO and $K_2O$ is below 1.5 %. It is the same as the composition of natron glass and its share is the lowest as 7.9 %. Of these, type III is divided into two types according to the content of MgO and $K_2O$. It is identified that manufacturing technique of type I and II is drawing and type III is casting method with microscopic investigations. Type II and III is estimated that raw materials is different because is confirmed in the majority of ruins in spite of the fact that distribution ratio is very low. So, red brown glass beads distributed in Korea Peninsula are divided into three types of glass culture.