This research has a main focus on providing fundamental data for on-the-spot industrial fields by comparing and contrasting physical properties of fluffy spun-like material. The fluffy spun-like yarn is developed as fluffy yarn similar to natural spun-like yarn by treating polyester(FDY and + type shaped DTY) with ATY machine. In this experiment, using ATY machine for raw material texturing, we produced two fluffy yarns: (i) + type shaped(50d/36f, DTY) as core yarn and 100d/192f FDY as effect yarn[ATY(D)], (ii) FDY(75/36) as core yarn and 100d/192f FDY [ATY(F)] as effect yarn. After producing thous yarns, we twisted them with 500T/M, 700T/M, 1000T/M, respectively. produced yarns through this process were used as the samples for this experiment. Even though the shrinkage of fluffy yarn ATY(F) and ATY(D) becomes high as treated temperature rises and treated time lengthens, it is more affected by treated temperature then by treated time. In this experiment, produced fluffy yarn[ATY(D)] shows a little high values for temperature, but almost same values for higher temperatures. When we compare ATY(F) with ATY(D) fluffy yarn shows more natural fluffy yarn surface structure like natural cotton. The shrinkage of 700T/M twisted ATY(D) fluffy yarn show about 11% under treated temperature $180^{circ}C$ and treated time 30min, and about 7% under $120^{circ}C$ and 30min, respectively. But the shrinkage of 1000T/M fluffy yarn shoes about 9% and 6% under same conditions. Regarding treated time, tenacity and initial modulus of ATY(D) fluffy yarn rise high until 30min, but do not show much increase above 30min. Regarding treated temperature, tenacity and initial modulus of it rise high aboyer $140^{circ}C$.