polyester형 polyurethane foam은 낮은 내가수분해성을 가지므로 quasi prepolymer법에 의한 acrylic polyol을 사용함으로써 극복될 수 있다. acrylic polyol을 함유한 polyurethane foam은 acrylic polyol 함량이 증가함에 따라 인장강도와 경도가 증가하였다. 하지만 split 인열강도와 인열강도는 약간씩 변화되었다. polyurethane foam의 내가수분해성은 인장강도의 손실 백분율로 측정하였으며 acrylic polyol 함량이 25.5g에서 102g으로 증가함에 따라 향상되었다.
Polyester type polyurethane foam has low hydrolysis resistance. It was overcome with addition of acrylic polyol by quasi prepolymer method. Tensile strength and hardness of polyurethane foam contained acrylic polyol was increased with increasing of acrylic polyol contents. But split tear strength and tear strength was slightly changed. Hydrolysis resistance of polyurethane foam was measured by loss % of tensile strength. It was improved with increasing of acrylic polyol contents from 25.5g to 102g.