The effects of process parameters for the formation of polypropylene film such as the polypropylene concentration in the solution, drying temperature for coating film, and variation of nano-silica content on the surface structure and property of polypropylene film have been studied. A super-hydrophobic polypropylene film with a maximum contact angle of $154^{circ}$ was obtained at the condition of a polypropylene concentration of 30 mg/mL, a drying temperature of $30^{circ}C$, a drying pressure of 93 mtorr for 90 min. The increase of a drying temperature reduced the contact angle by enhancing the surface smoothness of the film. The increase of nano-silica content in the composite film composed of polypropylene and silica changed the surface shape from microporous to microglobular, which led to increasing the contact angle and showed the super-hydrophobic surface property.