Fabric made of 100% silk was dyed with Undaria pinnatifida extracts under different conditions such as varing colorant concentration, temperature, time and dyebath pH. The dye uptake (K/S, value), CIE L*,a*,b* and Munsell values of the dyed samples and mordanted samples were measured. Colorfastness, antibacterial property and UV protection property were also evaluated. As colorants concentration increased, the dye uptake increased progressively and maximum color strength was obtained at 100% V/V. Dye uptake also increased with increasing temperature and time, and the maximum color strength was obtained at $80^{circ}C$ and 60min. With pre-mordanting, the color of the Al and Fe mordanted silk fabrics was yellow on the Munsell color system, while the Cu mordanted fabric was a greenish color. Al and Fe post-mordanted fabrics had a yellow tone, and the Cu post-mordanted fabric had a yellow greenish tone. The light fastness property of the Cu mordanted silk fabric was relatively good, The effect of Al and Fe mordanting on fastness was insignificant. The antibacterial activity of dyed and unmordanted silk fabric was excellent, whereas fabric dyed and mordanted with Undaria pinnatifida extract demonstrated superior ultraviolet protection.