In this research, split-type complex yarn of 20:80, 40:60, 50:50 nylon6/polyester composition ratio was used in order to impose unique sense on split-type complex woven. After treating both split-type complex yarn of each ratio and its produced woven in alkali solution, we got the following results by checking physical properties based on alkali proportion and treatment time. Under the condition of NaOH 20% in this experiment, it took approximately double time 20% loss of weight. The loss of weight became high when polyester proportion of N/P(nylon6/polyester) composition ratio was low, in the same fineness yarn. Even though polyester proportion was low, the loss of weight was low when the fineness was high. N/P division was well processed at about 25% loss of weight under the condition of NaOH 20%, treatment temperature $50^{circ}C$, and treatment time 60 minutes. The research provides that the loss of weight should be processed around treatment time 24 hours in the case of NaOH concentration 15%, and treatment time 15 hours in the case of NaOH concentration 18%, respectively, in order to achieve N/P woven division ratio of about 70%-80% in industrial fields.