The microwave absorption ($P_{tot}$), which is the double integration value of ferromagnetic resonance signal, propositional to the saturation magnetization, and the increase of the $P_{tot}$ measured during the thermal reaction time expect the growth process of the nanoparticles. Therefore, in this work, we measured the $P_{tot}$ in order to obtain the growth time of iron oxide nanoparticles after thermal decomposition of $Fe(acac)_3$ precursor at aging temperature $T_a=273$, 300 and $324^{circ}C$, respectively. The best condition for monodisperse nanoparticles was obtained at $T_a=300^{circ}C$, which condition showed the most rapid increase of $P_{tot}$ with thermal reaction time. Finally, the rapid growth rate was necessary condition for the synthesis of iron-oxide monodisperse nanoparticles.