This study examined the effect of chemical attack on the stress-strain relationship of alkali-activated Hwangtoh concrete. Water-to-binder ratio and air content were selected as mixture parameters. The stress-strain relationship of concrete was measured at chemical immersion times of 0, 7, 28, 56, and 91 days from an age of 28 days. Based on the test results, the reduction in compressive strength of alkali-activated hwangtoh concrete owing to chemical attack was formulated. In sddition the present study demonstrated that the stress-strain behavior of concrete under chemical attack is significantly dependent on the air content and chemical immersion time, indicating the rate of decrease of modulus of elasticity was greater than that of compressive strength at the same immersion time. As a result, the stress-strain behavior of concrete under chemical attack was significantly inconsistent with the conventional models specified in the CEB-FIP provision.