We investigated dielectric relaxation properties of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics by addition (0~0.3 wt%) of $(Ba,Ca)SiO_3$ glass frit. All composition of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ added $(Ba,Ca)SiO_3$ glass frit showed the same crystallographic properties, coexistence of orthorhombic and tetragonal phase. By increasing addition of $(Ba,Ca)SiO_3$ glass frit, the Curie temperatures of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were decreased, whereas maximum dielectric constants of $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were dramatically increased. Especially the deviations of Curie temperature $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics were increased by increasing amount of $(Ba,Ca)SiO_3$ glass frit, and it indicated that $0.95(Na_{0.5}K_{0.5})NbO_3-0.05BaTiO_3$ ceramics added $(Ba,Ca)SiO_3$ glass frit have relaxor characteristics.