This study manufactured a CIG-based composite coating layer utilizing a new warm spray process, and a mixed powder of Cu-20at.%Ga and Cu-20at.%In. In order to obtain the mixed powder with desired composition, the Cu-20at.%Ga and Cu-20at.%In powders were mixed with a 7:1 ratio. The mixed powder had an average particle size of $35.4{mu}m$. Through the utilization of a warm spray process, a CIG-based composite coating layer of $180{mu}m$ thickness could be manufactured on a pure Al matrix. To analyze the microstructure and phase, the warm sprayed coating layer underwent XRD, SEM/EDS and EMPA analyses. In addition, to improve the physical properties of the coating layer, an annealing heat treatment was conducted at temperatures of $200^{circ}C$, $400^{circ}C$ and $600^{circ}C$ for 1 hour each. The microstructure analysis identified ${alpha}$-Cu, $Cu_4In$ and $Cu_3Ga$ phases in the early mixed powder, while $Cu_4In$ disappeared, and additional $Cu_9In_4$ and $Cu_9Ga_4$ phases were identified in the warm sprayed coating layer. Porosity after annealing heat treatment reduced from 0.75% (warm sprayed coating layer) to 0.6% (after $600^{circ}C/1hr$. heat treatment), and hardness reduced from 288 Hv to 190 Hv. No significant phase changes were found after annealing heat treatment.