Partial replacement of cement with blast furnace slag has many advantages such as the reduction of construction fee, the decrease of hydration heat and the increase of long-term strength. Hence, slag is widely used in practice. This study investigates the effect of slag on the rheological properties of cement paste and mortar. Three different types of slag (BS1, BS2 and BS3) with five different contents (0, 20, 40, 60 and 80 wt.%) were used to replace the cement. Each type of slag has different fineness. Water to binder ratio was 0.5. Test results showed that the partial replacement of BS1 and BS2 decreased flow and increased O-lot flow time, whereas that of BS3 caused an opposite effect, i.e., increased flow and decreased O-lot flow time. It was found that there was a good corelation between the values of yield stress and flow.