PURPOSES : The objective of this study is to evaluate the bond strength of asphalt emulsions including polymer-modified emulsions for chip seals and fog seals using the bitumen bond strength (BBS) test. METHODS : For the laboratory testing, the Pneumatic Adhesion tensile Testing Instrument(PATTI) device is used to measure the bond strength between the asphalt emulsion and aggregate substrate based on the AASHTO TP-91. In order to conduct all the tests in controled condition, all test procedures are performed in the environmental chamber. The CRS-2L and the SBS CRS-2P emulsions are used as a polymer-modified emulsion, and then unmodified emulsion, the CRS-2, is compared for the evaluation of chip seal performance. For the fog seal performance evaluation, two types of polymer-modified emulsions and one of unmodified emulsion, the CSS-1H, are employed. For chip seal study, the BBS tests are performed at 30, 60, 120, and 240 minutes of curing times with curing and testing temperatures of $15^{circ}C$, $25^{circ}C$, and $35^{circ}C$. The fog seal tests are conducted at 30, 60, 90, 120, 180 minutes, and 24 hours with curing and testing temperatures of $25^{circ}C$, $30^{circ}C$, and $35^{circ}C$. RESULTS AND CONCLUSIONS : Overall, chip seal emulsions and fog seal emulsions show the similar bond strength trend. At the same testing condition, polymer-modified emulsions show better bond strength than unmodified emulsions. Also, there is no significant difference between polymer-modified emulsions. One of important findings is that the most bond strength reaches their final bond strength within one hour of curing time. Therefore, the early curing time plays a vital role in the performance of chip seals and fog seals.