This study was undertaken to examine the electrochemical corrosion properties of an $Co_{80}Nb_{10}B_{10}$ and $Co_{82}Nb_8B_{10}$ amorphous alloys prepared by melt-spinning method under various conditions. The potentiodynamic polarization responses at various levels of pH (pH 2, pH 7, pH 12) showed that the corrosion current rate of $Co_{80}Nb_{10}B_{10}$ alloy is lower than that of $Co_{82}Nb_8B_{10}$ alloy in all levels of pH, implying the general corrosion resistance of the alloy with higher Nb content is better than that with higher Co content. The pitting potential of $Co_{80}Nb_{10}B_{10}$ alloy was also better than that of $Co_{82}Nb_8B_{10}$, evidenced by the higher pitting potential. Nb is thought to be effective in increasing the protectiveness of the passive film and hence to improve the corrosion resistance of Co-Nb-B alloys.