$BaTiO_3$ nano powder can be synthesized by hydrate salt method at $120^{circ}C$ in air. Decreasing the thickness of thick film, the nano dielectric particle is needed in electronic ceramics. However, the synthesis of $BaTiO_3$ nano particle at low temperature in air and their mechanism were not reported enough. And ultrasonic treatment can be tried because of low temperature process in air. Therefore, in this study, the $BaTiO_3$ nano powder was synthesised with the synthesis time and ultrasonic treatment at $120^{circ}C$ in air. In the synthesis process, the effects of process were evaluated. From the experimental observation, the synthesis mechanism was proposed. The homogeneous $BaTiO_3$ particle was synthesised by KOH salt solution at $120^{circ}C$ for 1hour. It was conformed that the ultrasonic treatment effected on the increase of synthesis rate. After cutting the salt powder using FIB, $BaTiO_3$ nano particles observed homogeneously in the cross-section of the salt particle.