A process has been successfully used to manufacture 6061/Graphite composite material and the Graphite particles are distributed uniformly within the Al alloy matrix. The 6061 powders was mixed with natural Graphite particles in a ball milling blender and cold compacted specimens were extruded into rods 15mm in diameter at 450$^{circ}C$. The results showed that tensile properties of the composites with Graphite content have been reduced. The emergence of fine microstructures appeared to be related to the graphite volume. Heat-treated composites were found to possess good mechanical properties as compared with those of non heated composites. A model was used that the tensile strength of the composites would be estimated from the theoretical calculation and experimental data.