The purpose of this study was to investigate the change of 3 point bending properties of various nickel titanium wires after recycling. Four types of nickel-titanium (Align: martensitic type, NiTi, Optimahoy, Sentalloy: austenitic type) wires were divided to three groups: as-received condition (T0: control group), treated in artificial saliva for four weeks (T1) and autoclaved after being treated in artificial saliva (T2). Detrimental changes were observes for the selected mechanical properties in three point bending test. Loading force at 3mm deflection, unloading force at 3mm deflection, stress hysteresis, loading force at 1mm deflection, unloading force at 1mm deflection and stress hysteresis at 1mm deflection were calculated. The findings suggest that : 1. Aligh demonstrated statistically significant increase in loading force (P<0.05) and unloading force (P<0.01) at 3mm deflection after recycling(T2), but NiTi, Optimalloy and Sentalloy showed no statistically difference after recycling. 2. Align demonstrated statistically significant decrease in hysteresis(P<0.01) after recycling(T2) but NiTi, Optimalloy and Sentalloy showed no statistically significant difference after recycling. 3. All wires showed no statistically significant difference in loading force at 1mm deflection after recycling(T2). 4. Align demonstrated statistically significant decrease in unloading force in 1mm deflection (P<0.05) after recycling(T2) but NiTi, Optimalloy and Sentalloy showed no statistically difference after recycling. 5. Loading force and unloading force of T1 showed no significant change compared with those of T0, but loading force and unloading force of T2 showed significant changes compared with those of T0(P<0.05, P<0.01 respectively). 6. Align demonstrated a tendency to lose some of this pseudoelsticity in T1 and pseudoplasticity and pseudoelasticity in T2.
본 연구의 목적은 재생된 니켈-티타늄 호선의 3점 굴곡물성의 변화를 조사하여, 임상적으로 니켈-티타늄 호선을 재생하여 사용하는 것이 타당한지를 알아보는 것이다. 4종의 니켈-티타늄 호선(Align, NiTi, Optimallo, Sentalloy)을 처리전(T0: 대조군)과 인공타액에 4주간 처리한 군(T1),그리고 인공타액 처리 후 가압증기 멸균소독한 군(T2)으로 구분하여 3점 굴곡실험을 하였다. 3mm변형시의 loading force, unloading force, hysteresis와 1mm 변형시의 loading, unloding force, stress hysteresis의 변화를 관찰하여 다음과 같은 결과를 얻었다. 1. Align은 재생(T2)후에 3mm 변형시의 loading force, unloding force가 통계적으로 유의성있게 증가하였다(loading force: p<0.05, unloading force: p<0.01), NiTi, Optimalloy, Sentalloy에서는 통계적으로 유의성있는 차이가 보이지 않았다. 2. Align은 재생(T2)후에 hysteresis가 통계적으로 유의성있게 감소하였다(p<0.01). NiTi, Optimalloy, Sentalloy에서는 통계적으로 유의성있는 차이가 보이지 않았다. 3. 모든 호선에서 1mm변형시의 loding force는 재생(T2)후에 통계적으로 유의성있는 차이를 보이지 않았다. 4. Align은 재생(T2)후에 1mm 변형시의 unloading force가 통계적으로 유의성있게 증가하였다(p<0.05). NiTi, Optimalloy, Sentalloy에서는 통계적으로 유의성있는 차이가 보이지 않았다. 5. Align loading force와 unloading force는 T1과 T0는 통계적으로 유의한 차이가 없었으며, T2와 T0사이에 유의성 있는 차이가 있었다(각각 p<0.05, p<0.01). 6. Align은 T1에서 pseudoelasticity가 감소하고, T2에서는 pseudoplasticity와 pseudoelasticity가 감소하였다.