Acrylonitrile (AN)-acrylamide (AM) copolymers were prepared by nitric acidic hydrolysis of homopolyacrylonitrile. The acrylamino group increased as a function of hydrolysis time, while crystallinity decreased. Differential scanning calorimetry and a thermal gravimetric analysis indicated that the acylamino introduced by acidic hydrolysis effectively enhanced the cyclization reaction at low temperature due to the change of the cyclization reaction mechanism. Char-yield of AN-AM copolymers also gradually increased with increasing hydrolysis time. The maximum char-yield was 49.48% when hydrolized at 23°C in 65% nitric acid solution for 18 h, which was 30% higher than that of non-acidic hydrolysis of homopolyacrylonitrile. Simulation of the practical process also showed an increase of char yields, where the char yields were 55.43% and 62.60% for homopolyacrylonitrile and copolyacrylonitrile, respectively, with a hydrolysis time of 13 h.
1. Introduction 2. Experimental 2.1. Materials 2.2. Precipitation polymerization 2.3. Acidic hydrolysis of PAN 2.4. Characterization 3. Results and Discussion 3.1. Infrared spectroscopy 3.2. XRD 3.3. DSC analysis 3.4. TGA 4. Conclusions