The mechanical properties were measured for magnesium phosphate glasses containing small amounts of water. The decrease in hardness with increasing water content was resulted from a looser chain structure caused by water. The fracture of these glasses was changed from brittle fracture to plastic deformation as a results of the increased viscous flow with increasing water contents. The extent of any viscous flow or deformation initiating from the crack tips in these glasses could be considered as quite small.