The primary aim of this study was to access the degree of marginal leakage in composite resin inlay restorations. Class V cavities were prepared on sixty extracted premolars. They were classified as control group and experimental group 1, 2 and each group was filled with BIS-FIL $I^{(R)}$ and $Silux^{(R)}$ composite resins. In the control group, the composite resin was inserted directly, the experimental group 2 was inserted as composite resin inlay after heat treatment on $125^{circ}C$, 10 minutes. Then thermocycling was performed 1000 times. After staining with 1% Basic Fuchsin, they were cut in Buccolingual direction and the degree of penetration of the dye was examined under L/M. The following results were obtained : 1. In occlusal margin area, difference in marginal leakage was not observed in all groups. 2. In gingival margin area, cavities filled with composite resin inlay was less marginal leakage than filled directly in BIS-FIL $I^{(R)}$ group, and statistical significant difference was not existed in $Silux^{(R)}$ group. 3. The statistical significance was not existed between composite resin inlay and composite resin inlay heated secondarily. 4. In all groups, gingival margin area reveals more marginal leakage than occlusal margin area and statistical significance was existed.