Aluminum phosphate gel was synthesized by reacting aluminum sulfate as a soluble aluminum salt to tribasic sodium phosphate in this study. The optimal synthesis conditions based on the yield of product were investigated by applying Box-Wilson experimental design. It was found that optimal synthesis conditions were as follows: Reaction temperature; $61~71^{circ}C$, concentration of two reactants; 12.27~13.83%, concentration ratio of two reactants; [AI$_{2}$(SO$_{4}$)$_{3}$]/[Na$_{3}$PO$_{4}$]= 0.5, reaction time; 10.9~12.1 minutes, drying temperature of product; $60~72^{circ}C$. Aluminum phosphate gel prepared by the optimal synthesis conditions was suspended with four types of natural and synthetic gums at the concentration of 0.375~1.5wv%. Their Theological properties of aluminum phosphate gels were examined with Haake-Rotovisco RV 20 rotational viscometer. It showed that the higher concentration of suspending agents and lower temperature, the higher viscosity. Aluminum phosphate gel suspended by pectin and agar showed plastic flow with rheopexy, and their gels suspended by sodium alginate and sod. CMC showed plastic flow with thixotropy.