The isothermal oxidation behaviour of commercial superalloys produced in Korea was investigated by using Cahn-2000 microbalance in air at $1000^{circ}C$ and $1100^{circ}C$. The effect of alloying elements on the isothermal oxidation was studied by examination of the oxide structures, their morphologies, and EDS linescanning and mapping of cross-section of oxidized specimens. Generally, external Cr2O3 films were formed on all alloy surface, but were not pure, The effect on the oxidation behaviour of refractory elements such as Nb, Mo in Inconel 718 was considered to be deleterious, and the formation of internal Al oxide in Inconel 601 was beneficial.