$ LiNbO_3$ single crystals were grown using the Czochralski Method at various pulling speeds. Macroscopic defects such as cracks, bubbles and cellular structures were observed in some crystals. Cracks and bubbles observed in the crystals depended on the pulling speed and cooling rate. $ LiNbO_3$ crystals of about 15mm diameter could be grown properly at 6-7mm/h pulling speed and $ 20^{circ}C/h$ cooling rate. In order to investigate dielectric properties and optical properties for device application, these properties were measured for the sample cut along a axis and c axis at different temperatures.