Effect of agglomeration of $Nb_20_5$ of the same primary particle size on formation reaction and sintering of $Pb(Mg_{1/3};Nb_{2/3})O_3$ was examined. Both solid state reaction and molten salt synthesis were adopted. With decreasing agglomeration of $Nb_20_5$ increased the rate of formation reaction of perovskite PMN in solid state reaction, but had little influence in molten salt synthesis. It was concluded that the increase in the inhomogeneity of the dispersion state of intermediate pyrochlore with increasing agglomeration of $Nb_20_5$ retarded the formation reaction of perovskite PMN in solid state reaction, while had little influnce in molten salt synthesis due to its solution - precipitation mechanism -mainly depends on powder surface area.